本研究主要再探討使用石灰石粉分別以10％、20％、30％、40％取代水泥量，拌製標稱強度30 MPa之混凝土，同時將坍度控制在12 ± 1.5㎝，空氣含量4.5±1.0％下，進行混凝土之新拌性質、硬固性質及耐久性等試驗，以瞭解石灰石粉對混凝土之影響。
　　研究結果顯示，以石灰石粉取代水泥，可以縮短凝結時間，減少骨材析離及泌水現象的發生；對於早期強度略有提升但是在晚期強度的發展上並無顯著的效果；耐久性試驗如：磨耗試驗、吸水率、吸水速率、氯離子滲透及中性化深度上均明顯比控制組差。但體積穩定性則明顯的顯示出其乾縮量有降低的趨勢。

　　The main objective of this study is to research the influences of limestone on concrete by substituting limestone on the amount 10％, 20％, 30％, and 40% respectively for cement and to blend up the concrete with the normal strength is 30 MPa. In the same time, this test is on the condition that slump is 12 ± 1.5㎝,and air content is below 4.5±1.0％.
　　The result indicated that it would shorten setting time and decrease the segregation index and bleeding. Besides, it would improve the initial strength but not show obvious contribution on the later strength development. Results of durability test, such as abrasion, water absorption, Sorptivity, chloride penetration, and carbonization depth were inferior to which of the control. However, volume stability and drying shrinkage is lower than which of the control.

1.丁大鈞，「高性能混凝土講座 第九講 耐久性（四）-碳
化」，建築結構，第11期，(1997)。
2.小林一輔, “コソクリ一卜の碳酸化に關ある研究”,土
木學會論文集, Vol.15, NO.433, pp.1-14, (1991.8)。
3.川島滿成、金丸和光、張日紅，「高流動性混凝土工廠
製品之製造」，水泥、混凝土，NO.624，(1999)。
4.下田 孝，21世紀的水泥．コソクリート研究開發及水泥
產業之角色，水泥．混凝土635，pp.2-9，(2000)。
5.小津 博，山田一夫，矢野真弓，市川牧彥，汎用水泥的
3成分系混合水泥之提案-幾種的基礎物性-，水泥．混凝
土論文集，55，pp.89-95，(2001)。
6.水泥協會，石灰石微粉末委員會報告書，(2001)。
7.丸岡正知、藤原浩已、下山善秀、富田六郎，「石灰石
微粉末之各種特性與新拌性質之關係」，土木學會論文
集，NO.725，(2003.2)。
8.日本混凝土工學協會，「超流動混凝土研究委員會
書」，(1994.5)。
9.王櫻茂，「混凝土結構物的耐久性系列-鹼骨材反應
（Ⅰ）˙中性化（Ⅱ）」，成大土木結構材料試驗室，
台南，(2000)。
10.辰己正明，「世界最大之吊橋明石海峽大橋143萬方之
混凝土工事」，水泥、混凝土，NO.552，(1993)。
11.吳中偉、廖慧珍，「高性能混凝土」，中國鐵道出版
社，北京，(1999)。
12.沈得縣，「高爐熟料與飛灰之波索蘭反應機理及對水泥
漿體巨微觀性質影響之研究」，國立台灣科技大學，博
士論文，台北，(1999)。
13.林維民，「鋼筋混凝土中性化之探討」，結構工程，第
九卷，第一期，pp.103-115，(1994)。
14.板井悅郎、市川牧彥、大門正機，「石灰石微粉末之特
性及應用」，混凝土工學，Vol.36，(1998)。
15.星野清一、大場陽子、版井悅郎、大門正機，「添加石
灰石微粉末對混凝土特性變化之解析」，水泥、混凝土
論文集，Vol.50，(1996)。
16.城國省二，沢木大介，從21世紀所求之水泥像-歐洲汎
用水泥之解析，太平洋水泥研究報告，140，pp.4-24，
(2001)。
17.馬康俊，「鋼筋混凝土建築結構物中性化診斷模式之研
究-以台北地區為例」，台灣工業技術學院，碩士論
文，(1994)。
18.常冠群，「蒸氣催化含矽灰水泥漿體物理性質之研
究」，國立交通大學，碩士論文，新竹，(1980)。
19.張大鵬，「混凝土動彈性係數」，土木水利，第二十五
卷，第三期，pp.40-50，(1998)。
20.黃士元等，「近代混凝土技術」，陝西科學技術出版
社，西安，(1998)。
21.黃兆龍，「混凝土性質和行為」，詹氏出版社，
(1999)。
22.黃憲弘，「廢玻璃應用於混凝土骨材之研究」，國立雲
林科技大學，碩士論文，雲林，(2001)。
23.湛淵源、黃兆龍，「混凝土電阻性質與氯離子電滲行為
之探討」，土木水利，第十三卷，第二期，pp.293-
302，(2001)。
24.詹穎雯，「混凝土水中磨耗性質之研究」，專案研究報
告，財團法人中興工程顧問社，台北，(1997)。
25.廖肇昌，「國內混凝土耐久性規範探討」，混凝土結構
耐久性技術，台灣營建研究院，台北，(2000)。
26.劉俊杰，「水泥漿體孔隙與水灰比及抗壓強度關係之研
究」，國立台灣科技大學，碩士論文，台北，(1980)。
27.蔣國鈺、王櫻茂，「混泥土質流行為與耐久性之關
係」，碩士論文，成功大學，台南，(2000)。
28.蘇南，「二十一世紀TAICON（台灣混凝土）之配比設
計」，高性能混凝土配比 設計實作研討會，台北，7
月，pp.45-70，(1988)。
29.A.M.Neville, W.H.Dilger, J.J.Brooks, “Creep of
Plain and Strucctural Concrete,”(1983).
30.ACI Committee 209R,“Prediction of Creep,
Shrinkage and Temperature Effects in Concrete
Structures,” ACI manual of concrete
practice,(1989).
31.ACI Committee 201，“Guide to Durable
Concrete,” ACI Materials Journal, Vol.88, No.5,
Sep-Oct, pp.544-582,(1991).
32.Andrade,“Calculation of chloride diffusion
coefficient in concrete from ionic migration
measurement,”Cement and Concrete Research,
Vol.23, pp.724-742,(1993).
33.C.Hall, “Water sorptivity of mortars and
concretes: a review,” Magazine of Concrete
Research, 41, No.147,(1989).
34.EN197-1：2000, cement – Part1：Composition,
Specifications and Conformity Criteria for
common Cements, European Standards, (2000).
35.Frederick, J.R.,“Ultrasonic Engineering,”
John-Wiley & Sons, Inc.,(1965)。
36.Hiroyuki O., Shigeyoshi N.,“Prediction and
Evaluation of the Depth of Carbonation of
Concrete by Accelerated Test,” Journal of
structural mechanics and earthquake engineering,
Vol.8, NO.390, pp.225-233,(1998).
37.Jazairi, B.E. and J.M. Illston,“The Hydration
of Cement paste Using The Semi-Isothermal Method
of Derivatite Thermogravity,”Cement and
Concrete Research, Vol.10, pp.361~366,(1980).
38.Jong H. C. and Taketo U.“Relation between Phase
Composition, Pore Structure and Compressive
Strength of Carbonation Mortar,” J. Materials.
Conc. Struct. Pavements, Vol.29, NO.526,
pp.133-141, Novermber (1995).
39.J.Francis Young, et al.,The Science and
Technology of Civil Engineering Materials,
Prentice-Hall Inc., New Jersey,(1998).
40.Leslie, J.R., and Cheesman, W.J.,“An Ultrasonic
Method of studying Deterioration and cracking in
Concrete structure,” ACI Journal Proceeding,
Vol.46, NO.1, pp.17-36.
41.Mindness, S & J.F. Young,“Concrete,”Ibid,
pp.203-222,(1981).
42.Meyers, M.A.,“Dynamics Behaviors of
Materials,”John-Wiley & Sons, Inc.,(1994)。
43.Okmura H., ”Self compacting High Performance
concrete,” ACI Concrete International,
July,(1997).
44.P.K.Mehta, Concrete Structure, Properties, and
Materials, Prentice-Hall Inc., New
Jersey,(1980).
45.S. Tsivilis, G. Batis, E. Chaniotakis, Gr.
Grigoriadis, D. Theodossis, “Properties and
behavior of limestone cement concrete and
mortar,”Cement and Concrete Research,
pp.1679-1683,(2000).
46.R. Feldman, L. R. Prudencio J. , G. Chan,“Rapid
chloride permeability test on blended cement and
other concrete: correlations between charge,
initial current and conductivity,”Construction
and Building Materials, Vol.13,
pp.149-154,(1999).
47.Smerda Zdenek/Kristek Vladimir, “Creep and
shrinkage of concrete elements and structures,”
Elsevier,(1988).
48.Vagelis G. Papadakis, Costas G. Vayenas, and
Michael N. Fardis, “Fundamental Modeling and
Experimental Investigation of the Concrete
Carbonation,”ACI Materials Journal, Vol.88,
NO.4, pp.363-373,(1991).
49.Vagelis G. Papadakis, Costas G. Vayenas, and
Michael N. Fardis,“A Reaction Engineering
Approach to the problem of the Concrete
Carbonation,”AICHE Journal, Vol.35, NO.10,
pp.1639-1650,(1998).
50.Y.H.Loo, M.S.Chin, C.T.Tam, K.C.G.Ong,“A
Carbonation Prediction Model for Accelerated
Carbonation Testing of the Concrete,”Magazine
of Concrete Research, 46(168), pp.191-200,
(1994).