隨著塑膠高分子成型技術日益提升，生產的零件也趨精密微小化，射出成型已成為製造業重要的生產過程，可以大量生產，所需成本低且快速，因此微射出成型的技術因而更為重要。本研究延續以前之微結構射出成型模具以及快速加熱裝置，並裝置模內溫度感測器。模仁的部分採高真空濺鍍方式將石墨碳鍍於模仁表面0.1μm，然後進行射出成型的實驗。主要探討比較有鍍碳模仁與無鍍碳模仁透過快速加熱系統加熱，對於微結構模仁滯熱後的充填效果，以得到較高的充填，並利用模內的溫度感測器，了解微射出成型模具溫度必須高於玻璃轉移溫度，才能對微結構充填完整。

Due to the improvement of injection molding technology, a lot of products become smaller and more delicate.The micro-injection molding gradually plays a major role in the mass production. This study utilized the surface rapid heating system to understand the heating effect on the micro-injection molding. A graphite thin film (0.1μm thickness) was coated onto the surface of insert the mold by ion sputtering to enhance the heat absorption during the infrared heating.Space the result shows that the injection process was enhanced by the graphite coating as well as the surface rapid heating system. In addition, the cavity temperature sensor indicates that the temperature of the mold is needed to be higher than the glass transition temperature to have a complete molding.

參考文獻
[1]陳建人,“微機電系統技術與應用”,行政院國家科學委員會精密儀器發展中心,民國92年7月。
[2]鐘享年,“微量射出成形製程設備技術”,工業技術研究院機械工業研究所 , 民國92年4月。
[3]M.S.Despa, K.W.Kelly and J.R.Collier, “Injection molding of polymeric LIGA HARMs”, Microsystem Technologies, 6, pp60-66 (1999)。
[4]Dong-Hak Kim, Myung-Ho Kang and Y.H.Chun,”Development of a new Injection Molding Technology Momentary Mold Surface Heating Process,”Journal of Injection Molding Technology,5,No.4,pp229(2001)。
[5]Donggang Yao and Byung Kim,”Development of Rapid Heating and Colling System for Injection Molding Application,”Polymer Engineering and Science,42,No,12(2002)。
[6]李育芸,“感應加熱應用於模具加熱之研究”,碩士論文,私立中原大學,民國91年7月。
[7]葛紹岩 那鴻悅,”熱輻射性質及量測”,科學出版社,中國(1989)。
[8]A.B. Frazier, M.G, Allen “High aspect ratio electroplated microstructures using a photosensitive polyimide process”, Micro Electro Mechanical Systems, 1, pp87-92 (1992)。
[9]林志鴻,”微射出快速模溫控制系統與玻璃模仁表面結構複製成型探討”,碩士論文,國立台灣大學(2001)。
[10]楊益成,”輻射快速加熱模具表面之實驗研究”, 成功大學工學科學研究所碩士論文, 民國94年6月
[11]張弘超,”射出成形製程參數對為特徵孔洞充填影響”, 成功大學航空太空工程研究所碩士論文, 民國93年6月。
[12]http://www.bluegiant.com.tw/nhsonih.htm,民國95年4月。
[13]林晃業,”微米級結構射出成型之研究”, 成功大學航空太空工程研究所碩士論文, 民國94年6月。
[14]游茗景,”快速加熱系統於微射出成型之應用”, 成功大學航空太空工程研究所碩士論文, 民國94年6月。
[15]環球奈米科技公司鍍碳製成簡介。
[16]賴耿陽, ”薄膜製作工藝學”,復漢出版社,1987/2