摘要
　　排水瀝青混凝土中，一般規定須添加一定比例之填充料，且對填充料之性質有一定之要求，目前多採用潔淨的石粉取代＃200號篩以下之細料做為填充。由於石粉之成本較高，拌合廠多半用乾拌粒料的程序中所回收之粉塵做為填充料，造成拌合廠及試驗室中所製成之瀝青混凝土其性質有所差異。
　　本研究分兩方面探討填充料對排水性瀝青混凝土之影響，分別為填充料種類以及添加比例，配合一般排水瀝青配合設計之試驗項目，探討瀝青混凝土之性質，了解填充料之比例與種類何者影響瀝青混凝土較顯著，若填充料比利影響較顯著，則日後將不必要求須以石粉做為填充料，反之則更需注意拌合廠填充料之品質管理。
　　研究結果發現，填充料之種類只影響瀝青混凝土之排水性質，使用石粉得到較佳的排水性質；填充料之比例則主要影響瀝青混凝土之強度及抗磨損率，提高填充料之添加比例，能有效增加強度及抗磨損之能力。

Abstract
In the Drainage Pavement, the general regulation must add filler of certain proportion , and have certain requests to the fillers , adopt the clean stone powder to replace the fillers which pass #200 sieve. Because the cost of the stone powder is relatively high, so the factory always use the dust to replace the stone fillers, it cause the different between asphalt concrete which at field and factory.
This research divides into two respects about the influence of fillers on the Drainage Pavement , material kind and add the proportion respectively , cooperate with and generally specification of Drainage pavement.
The result of study finds, that the kind of the material only influences the nature that draining of water, use the stone powder to receive better water drainage nature; the proportion of the material influences the wearing and tearing rate, improve the proportion of fillers, can increase the intensity and resist the ability to wear and tear effectively .

參考文獻

1. 日本道路協會，「排水性鋪裝技術指針」，1996。
2. 方楷逸，「改質瀝青應用於排水級配之抗水侵害研究」，國立成功大學土木研究所碩士論文，台南，2002。
3. 朱柏彥，「骨材級配對排水瀝青混凝土成效之影響」國立成功大學土木研究所碩士論文，台南，2003。
4. 李金鴻，「粗骨材性質與夯壓溫度對排水性瀝青混凝土性質之研究」，國立成功大學土木研究所碩士論文，台南，2002。
5. 林昶穆，「不同配合設計方法對排水瀝青混凝土成效之比較」，國立成功大學土木研究所碩士論文，台南，2003。
6. 林祐徵，「細粒料多角性與限制區對瀝青混凝土抗變形之影響」，國立成功大學土木研究所碩士論文，台南，2000。
7. 張聰裕，「中鋼細爐渣做瀝青砂砂料之效果研究」，國立成功大學土木研究所碩士論文，台南，，1981。
8. 盧俊愷，「利用中鋼爐渣做瀝青混凝土級配料之效果研究」，國立成功大學土木研究所碩士論文，台南，，1981。
9. 王建偉，「添加纖維對排水性瀝青混凝土成效之影響」，國立成功大學土木研究所碩士論文，台南，2004。
10. 林佑諭，「排水性瀝青混凝土老化之研究」，國立成功大學土木研究所碩士論文，台南，2004。
11. 陳秀珍，「排水瀝青混凝土與再生排水瀝青混凝土抗水侵害之研究」，國立成功大學土木研究所碩士論文，台南，2004。
12. 潘厚志，「VMA變化對於瀝青混凝土性質之影響」，國立成功大學土木研究所碩士論文，台南，2004。
13. 許志淇，「粗粒料骨材性質對瀝青混凝土抗變形能力之研究」，國立成功大學土木研究所碩士論文，台南，2001。
14. 蔡攀鰲，「瀝青混凝土」三民書局，台北，1985。
15. 俞大彥，「填充料對纖維改質瀝青混凝土工程性質影響之研究」，國立中央大學土木研究所碩士論文，中壢，1994。
16. Akhtarhusein A, Tayebali, Glen A, Maipass, and N. Paul Khusla, “Effective of Mineral Filler Type and Amount on the Design and Performance of Asphalt Concrete Mixtures” Transportation Research Board 77th Annual Meeting January 11-15, 1998 Washington, D.C.
17. Anderson D, A,. Tarris, J, P, and Brock, J. D., “Dust Collocter Fines and their Influence on Mixture Design” AAPT, Vol. 51, pp. 363-397,
(1982)
18. Galal, Khaled A. and Thomas D. White. “Correlations Between Superpave Asphalt Stiffnesses and In-Service Pavement Performance” Transportation Research Record 1766, pp.57-65 (2001)
19. Kandhal, Prithvi S., and L. Allen Cooley, Jr., ”Coarse- Versus Fine-Graded Superpave Mixtures”, Transportation Research Record 1789, pp 215-224 (2002).
20. Kandahal, P. S., and L. A. Cooley, Jr. NCHRP Report 464. “The Restricted Zone in the Superpave Aggregate Gradation Specification.” TRB, National Research Council, Washington, D.C., (2001).
21. Kim, Yong-Rak, Dallas N. Littil, and Injun Song, ”Effective of
Mineral Fillers on Fatigue Resistance and Fundamental Material
Characteristics”, Transportation Research Record 1832, pp1-8
(2003).
22. Lesueur, D., and D. N. Little. “Effective of Hydrated Lime on Rheology, Fracture, and Aging of Bituminous Paving Mixtures” TRB, National Research Council, Washington D.C., pp. 93-105 (1999)
23. Peter E. Sebaaly, Edgard Hitti, and Dean Weitzel, “Effective of Lime in Hot-Mix Asphalt Pavements”, Transportation Research Record
1832, pp 34-41 (2003).
24. Richardson, C., “The Morden Asphalt Pavement” New York, John Wilwy and Sons (1914)
25. Rigden, P. J., Road Research Technical Paper No.28, Road Research Laboratory, Hammonsworth, Middlesex, U. K. (1954)
26. Roberts,F.L.,P.S.Kandhal,E.r.Brown,D.Y.Lee,T.W.Kennedy. “HOT MIX ASPHALT MATERIALS,MISTURE DESIGN,AND CONSTRUCTION,”NAPA Education Foundation ,Lanham,Maryland,(1996).
27. Winniford, R. S.. “The Rheology of Asphalt Filler System as Shown in Microviscosimeter” ASTM STP 390 (1961)
28. Zeng, Menglan and Khaled Ksaibati, “Evaluation of Moisture Susceptibility of Asphalt Mixtures Containing Bottom Ash”, Transportation Research Record 1832, pp.25-33 (2003).